DX51D Galvanized Strip Production Process

Production process:
The first stage: pickling and decontamination of the whole roll of strip steel to make the surface bright and clean.
The second stage: after pickling, it is cleaned in ammonium chloride or zinc chloride aqueous solution or mixed ammonium chloride and zinc chloride aqueous solution tank, and then sent to the hot dip tank for galvanizing.
The third stage: after the strip steel is galvanized, it is rolled up and put into storage. The galvanized layer can generally not be less than 500g/m2 according to the customer's needs, and any sample shall not be less than 480g/m2.
Post treatment of galvanized strip steel includes passivation, pre phosphating and oiling. First of all, passivation treatment should be carried out on the galvanized strip steel, which can improve the surface structure and luster of the zinc coating, improve the corrosion resistance and service life of the zinc coating, and improve the adhesion between the coating and the base metal. The chromate passivation treatment is mainly used. Some activators, such as fluoride, phosphoric acid or sulfuric acid, are added to the passivation solution to obtain a thicker chromate film after passivation. When there is fluoride in the passivation solution, the surface tension of the steel strip can be reduced, the film forming reaction can be accelerated, and the chemical polishing effect can be increased to make the passivation film fine and bright.

Hot Tags: dx51d galvanized strip production process, China dx51d galvanized strip production process manufacturers, suppliers, factory, ASTM A53 Gr A Hot Rolled Galvanized Steel Pipe, Q345B Galvanized Steel Pipe, EN10210 Hot Dip Galvanized Oil Drilling Pipe, ASTM A53 GI Galvanized Steel Pipe, Sch 40 80 Seamless Galvanized Steel Pipe