S280GD Galvanized Steel Coil
Hot-dip galvanized steel S280GD in accordance with the EN 10346 standard is a high-quality structural steel that has been specially developed for use in structural engineering and building construction. With the material number 1.0244, S280GD has a minimum yield strength Rp0.2 of 280 N/mm² and thus joins the higher strength classes of galvanized structural steels. Hot-dip galvanizing in accordance with EN 10346 guarantees a uniform zinc coating on the steel surface, which effectively protects the base material against corrosion. Thanks to the various coating systems (+Z, +ZF, +ZA, +ZM, +AZ and +AS), the material can be precisely adapted to different climatic and mechanical stresses.
S280GD Galvanized Steel Coil Chemical Composition
| Element | Content (weight%) |
| Carbon (C) | ≤ 0.20 |
| Manganese (Mn) | ≤ 1.70 |
| Phosphorus (P) | ≤ 0.10 |
| Sulfur (S) | ≤ 0.045 |
| Silicon (Si) | ≤ 0.60 |
S280GD Galvanized Steel Coil Mecahmical Properties
| Property | Value | |
| Tensile Strength (Rm) | 360 MPa | |
| 0.2% Proof Strength (Rp0.2) | 280 MPa | |
| Min. Elongation (A, Lo = 80 mm) | – | 18% |
| 0.5mm < t ≤ 0.7mm | 16% | |
| 0.35mm < t ≤ 0.5mm | 14% | |
| t ≤ 0.35mm | 11% | |
| Bending Center Diameter (mm) | 1a | |
| S280GD tensile strength can range up to 140 MPa, depending on the specific material grade and processing conditions. | ||
Properties
S280GD impresses with a balanced combination of high strength and good formability. The minimum yield strength Rp0.2 of 280 N/mm² and a characteristic tensile strength of at least 360 N/mm² ensure reliable load-bearing capacity even under dynamic load conditions. At the same time, the hot-dip galvanized surface enables an extended service life in corrosive environments.
The different cover variants offer specific advantages:
+Z (pure galvanized):
Standard corrosion protection for general conditions.
+ZF (zinc-iron):
Improved coating adhesion and increased resistance to mechanical stress.
+ZA (zinc-aluminium):
Optimized resistance in atmospheric environments.
+ZM (zinc-magnesium):
Extended protection in maritime and saline zones through passivating behavior.
+AZ (aluminum-zinc):
Combination of heat resistance and corrosion protection, ideal for high surface temperatures.
+AS (aluminum-silicon):
Especially for applications with extreme temperature influences and high corrosion loads.
S280GD is also characterized by its good weldability, homogeneous microstructure and reliable dimensional stability, which ensures precise further processing in profiling, bending and welding processes.
S280GD Steel Applications
- Construction: Structural frameworks, roofing systems, wall panels, steel decking, and facade elements.
- Automotive: Underbody components, reinforcements, brackets, door panels, and exhaust system parts.
- Appliances: Washing machine drums, dryer housings, refrigerator panels, HVAC enclosures, and water heater tanks.
- Agricultural Equipment: Silos, storage bins, farming machinery components, and greenhouse structures.
|
Standard |
Grade |
C |
Si |
Mn |
P |
S |
Ti |
|
Forcold Forming Chinese Standard |
DX51D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
DX52D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX53D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX54D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX56D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
DX57D+Z |
0.12 |
0.50 |
0.60 |
0.100 |
0.045 |
0.30 |
|
|
Forcold Forming Japanese Standard |
SGCC |
0.15 |
0.50 |
0.80 |
0.050 |
0.030 |
0.025 |
|
SGCD1 |
0.12 |
0.50 |
0.60 |
0.040 |
0.030 |
0.025 |
|
|
SGCD3 |
0.08 |
0.50 |
0.45 |
0.030 |
0.030 |
0.025 |
|
|
SGCD4 |
0.06 |
0.50 |
0.45 |
0.030 |
0.030 |
0.025 |
|
|
For Structure Japanese Standard |
SGC340 |
0.25 |
0.50 |
1.70 |
0.200 |
0.035 |
0.025 |
|
SGC400 |
0.25 |
0.50 |
1.70 |
0.200 |
0.035 |
0.150 |
|
|
SGC490 |
0.30 |
0.50 |
2.00 |
0.200 |
0.035 |
0.025 |
|
|
SGC510 |
0.30 |
0.50 |
2.50 |
0.200 |
0.035 |
0.025 |
|
|
For Structure AISI Standard |
S220GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
S250GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S280GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S320GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.025 |
|
|
S350GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.150 |
|
|
S550GD+Z |
0.20 |
0.60 |
0.70 |
0.100 |
0.045 |
0.150 |
FAQ:
What is the material number for S280GD?
The steel number equivalent is 1.0244.
What are common coating types available on S280GD?
S280GD can be galvanized with pure zinc (+Z), zinc-iron (+ZF), zinc-aluminum (+ZA), zinc-magnesium (+ZM), aluminum-zinc (+AZ) and aluminum-silicon (+AS).
What is the minimum yield strength of S280GD?
Minimum yield strength (Rp0.2) is 280 MPa.
What is the typical tensile strength?
Minimum tensile strength is around 360 MPa.
What is the minimum elongation?
Minimum elongation A80 is typically 18 % (varies slightly with thickness).